Дела о компании Dispersant Recommendations for White Paint in Thermoplastic Acrylic System

Dispersant Recommendations for White Paint in Thermoplastic Acrylic System

2026-06-15

Yuanbang 2650DB resin is a thermoplastic acrylic resin.

Parameter	Value
Appearance	Water-white to light yellow transparent liquid
Solid content	50±1%
Viscosity (25°C, Gardner)	10–20 S
Acid value	3 mg KOH/g
Hydroxyl value	—
TG	40°C
Solvent	Xylene, S-100

Viscosity of White Paste in Thermoplastic Acrylic Resin System Before and After Hot Storage

последний случай компании о Dispersant Recommendations for White Paint in Thermoplastic Acrylic System 0

Test Method	Store at 60°C for 7 days, measure viscosity change
Test Results	6915 and 6916 show good performance in both viscosity reduction and post-thickening control; 6110S shows high viscosity both before and after hot storage
Performance Rating	6110	6110S	6402	6110A	6915	6916	6976A	6500-50
	6	2	6	8	6	8	4	6
8 — Best, 6 — Good, 4 — Fair, 2 — Poor

Gloss of White Paste in Thermoplastic Acrylic Resin System Before and After Hot Storage

последний случай компании о Dispersant Recommendations for White Paint in Thermoplastic Acrylic System 1

Test Method	Store at 60°C for 7 days, measure gloss change
Test Results	6915 shows good performance in both 20° and 60° gloss; 6110S is significantly worse than others
Performance Rating	6110	6110S	6402	6110A	6915	6916	6976A	6500-50
	4	2	4	4	8	6	4	6
8 — Best, 6 — Good, 4 — Fair, 2 — Poor

L-Value of White Paste in Thermoplastic Acrylic Resin System Before and After Hot Storage

последний случай компании о Dispersant Recommendations for White Paint in Thermoplastic Acrylic System 3

Test Method	Store at 60°C for 7 days, measure L-value change
Test Results	6402 and 6110A show good L-value performance
Performance Rating	6110	6110S	6402	6110A	6915	6916	6976A	6500-50
	4	4	8	8	4	6	4	4
8 — Best, 6 — Good, 4 — Fair, 2 — Poor

Dispersant Recommendations for White Paint in Thermoplastic Acrylic System

6916 — The First Choice for Extreme Viscosity Reduction & High Gloss

Core Advantage: Extreme viscosity reduction and high gloss.

Viscosity Control:
After 7 days of hot storage, the viscosity did not increase but actually decreased to 1,328 mPa·s (initial viscosity: 3,237 mPa·s) — the lowest viscosity after hot storage among all dispersants tested.

Appearance Performance:
Achieves the highest 20° gloss (98.2) and L-value (93.84) in the system.

Conclusion:
If you pursue the best application flowability (low viscosity) and final film appearance (high gloss, high distinctness of image), 6916 is the absolute first choice.

6915 & 6500-50 — Excellent and Stable Backup Options

These two dispersants deliver excellent and stable performance, making them reliable backup choices.

Common Features:

Parameter	Performance
Viscosity Control	Viscosity after hot storage stabilizes at approximately 1,881 mPa·s — not as extreme as 6916, but far better than other dispersants
Appearance Performance	L-value remains above 93.7, with excellent gloss (108–110) as well

Conclusion:
Performance is second only to 6916, suitable for applications with high requirements for gloss and leveling.

События

Новости

Случаи

Контакты

Контакты: Ms. Anna

Телефон: 86-0711-5117111

Факс: 86-0711-3809626

Свяжитесь сейчас

Перешлите нас

Полимерное рассеивающее средство

Рассеивающее вещество пигмента

Дисперсия наночастиц

Рассеивающее вещество краски

Увлажняющее и рассеивающее средство

Диспергент пигмента в воде

Унивелирующий агент

Противоустроительный агент

Тиксотропный агент

дефугатор Добавка

Промотор сцепления

Диспергент общего назначения

Добавки краски на водной основе

Добавки краски на масляной основе

Дисперсия полиэтиленового воска

Концентрат суспензии

Полимерное рассеивающее средство

Рассеивающее вещество пигмента

Дисперсия наночастиц

Рассеивающее вещество краски

Увлажняющее и рассеивающее средство

Диспергент пигмента в воде

Унивелирующий агент

Противоустроительный агент

Тиксотропный агент

дефугатор Добавка

Промотор сцепления

Диспергент общего назначения

Добавки краски на водной основе

Добавки краски на масляной основе

Дисперсия полиэтиленового воска

Концентрат суспензии

Dispersant Recommendations for White Paint in Thermoplastic Acrylic System

Новости

Случаи

Полимерное рассеивающее средство

Рассеивающее вещество пигмента

Дисперсия наночастиц

Рассеивающее вещество краски

Увлажняющее и рассеивающее средство

Диспергент пигмента в воде